Home > products > Aluminium Hydroxide Powder > Flame Retardant Ath Alumina Trihydrate , Al2(OH)3 Aluminum Hydroxide Powder

Flame Retardant Ath Alumina Trihydrate , Al2(OH)3 Aluminum Hydroxide Powder

Product Details

Place of Origin: Jiaozuo Henan, China

Brand Name: Eversim

Certification: ISO 9001

Model Number: Grade 1

Payment & Shipping Terms

Minimum Order Quantity: 1 ton

Packaging Details: according to your demands

Delivery Time: 3-5 days

Payment Terms: L/C, D/A, D/P, T/T, Western Union, MoneyGram

Supply Ability: 1000 tons per month

Get Best Price
Highlight:

aluminum hydroxide compound

,

ath alumina trihydrate

Customs Code:
2818300000
MF:
Al2(OH)3
MW:
77.98980
Appearance:
White Powder
Purity:
99.6%
Density:
2.42 G/cm3
Melting Point:
300°C
Certificate:
SGS
Boiling Point:
Not Applicable
Color:
White
Flash Point:
Not Applicable
Form:
Powder
Melting Point:
600-700°C
Molecular Formula:
Al(OH)3
Molecular Weight:
78.00 G/mol
Name:
Aluminium Hydroxide Powder
Odor:
Odorless
Shelf Life:
2 Years
Solubility:
Insoluble In Water
Storage Temperature:
Room Temperature
Uses:
Used As A Flame Retardant And As An Antacid
PH:
7.0-8.5
Customs Code:
2818300000
MF:
Al2(OH)3
MW:
77.98980
Appearance:
White Powder
Purity:
99.6%
Density:
2.42 G/cm3
Melting Point:
300°C
Certificate:
SGS
Boiling Point:
Not Applicable
Color:
White
Flash Point:
Not Applicable
Form:
Powder
Melting Point:
600-700°C
Molecular Formula:
Al(OH)3
Molecular Weight:
78.00 G/mol
Name:
Aluminium Hydroxide Powder
Odor:
Odorless
Shelf Life:
2 Years
Solubility:
Insoluble In Water
Storage Temperature:
Room Temperature
Uses:
Used As A Flame Retardant And As An Antacid
PH:
7.0-8.5
Flame Retardant Ath Alumina Trihydrate , Al2(OH)3 Aluminum Hydroxide Powder

Inorganic flame retardant additive alumina trihydrate aluminium hydroxide powder

 

 

Aluminum hydroxide flame retardant, not only has the function of non-toxic, good stability, does not produce toxic gases at high temperature, but also reduce the advantages of plastic burning smoke emission, and low-temperature endothermic dehydration, at about 235-350℃. The aluminum hydroxide flame retardant polyolefin can be used as building materials and interior decoration materials of the automobile, ship, etc.
It is widely used in artificial marble, wire and cable, resin, rubber, plastic and other environmentally friendly flame retardant.

The special aluminum hydroxide sintering production process, the low iron content of aluminum hydroxide, high whiteness, can be used to produce solid surface materials (artificial marble) polyester resin or acrylic resin with the filler, the basic raw material of toothpaste. Widely used in artificial marble, DuPont, rubber, plastic, resin crafts, etc.

Low iron content agate grade aluminum hydroxide, high whiteness, it is the good material to produce solid surface materials (artificial marble) with polyester resin filler, toothpaste, artificial agate raw materials etc. The artificial agate made from this kind of ATH will be in good brightness and smooth surface, good abrasion resistance, stain resistance, impact resistance, high structural strength, is good filler in ideal modern new building materials and technology.

This product is low sodium content in ferrosilicon powder, can improve the optical properties of glass, reduce the swelling rate, whiteness, transparency, gloss, brightness enhancement of thermal shock resistance and chemical corrosion resistance can increase the glass.

Micron aluminum hydroxide property is to flame retardant self-extinguishing, thus adding advanced composite materials in the plastic and rubber products, it will not only have the function of flame retardant and smoke suppression effect but also anti-leakage resistance, abrasion resistance enhancement.

 

 

High whiteness aluminum hydroxide wet powder. Its appearance is white crystal powder, non-toxic and odorless, with the characteristics of high whiteness, low alkali and low iron.

 

 

Al(OH)3 99.8% min
Al2O3 64.8% min
SiO2 0.03% max
Fe2O3 0.01% max
Na2O 0.4% max
Moisture 12% max
L.O.I. 34-35%max
Whiteness 90%min
Particle size D50um

 

75-105

 

 

 

ITEM NO. Chemical Composition Physical Components
Al(OH)3%
SiO2 %
Fe2O3 %
NaO2%
S-Na2O (%)
Moisture(%)
L.O.I (%)
D50 um

Whiteness

(%)≥

DOP ml/100g

Black Spot

(P/100g)≤

Refaractive Index
LXH-WF-75 99.6 0.04 0.01 0.20 0.0007 0.08 35 75 94 21 20 1.57
LXH-WF-25 99.6 0.04 0.01 0.20 0.015 0.14 35 25 98 24 20 1.57
LXH-WF-10 99.6 0.04 0.01 0.20 0.20 0.2 35 9 99 33 20 1.57
LXH-WF-5 99.6 0.04 0.01 0.2 0.015 0.25 35 5 99 38 20 1.57
LXH-WF-2 99.6 0.04 0.01 0.2 0.03 0.3 35 2 99 45 20 1.57
LXH-WF-15 99.6 0.04 0.01 0.2 0.015 0.15 35 15 98 28 20 1.57